This technique is an alternative to traditionalPlating, Hot dip galvanized mechanical galvanizing equipment; at room temperature without external electric field of the solution, depend onRollerMechanical rolling energy and rubbing crushed glass beads, using the surface energy, forming a grinding collision and rubbing the role of multiphase flow environment, according to a predetermined thickness by adding zinc powder and zinc pharmaceutical, chemical deposition and mechanical collisions in the common formed under the action of surface smooth and shining the zinc coating. The process is completely different from the traditional theoryPlatingAnd hot dip plating, low cost, little pollution, coating thickness can be controlled in 5 to 100 microns, the room temperature operation, no hydrogen embrittlement, high efficiency, resistance to more than 300 hours of neutral salt spray test, quality, and consistent with the United States ASTMB695-8212 military C-81562, China A29JB/T8928-1999 standards.

     The technology used by the activated metal (zinc, aluminum, copper) powder can surface brightness close to the electro-galvanized, as needed, but pure zinc coating, zinc-aluminum coating, the surface can bePassivationClosed, etc., applicable to all kinds of mechanical processing workpiece surface finishing and protection, such as high strength bolts, screws, pipe fittings, nail, swing chains and other iron-based artifacts, especially washer and flexible workpiece. That the new technology products have been exported to the U.S., Australia and other countries, and for the countryHome AppliancesNetwork reconstruction, highway and other key projects.EconomyBenefits: to highway guard rail bolt, for example, the minimum thickness of zinc coating 50μm, using special mechanical plating equipment, the rated power 4kw / h, the two workers. Each processing 500kg, the whole process of 40 ~ 45min, the production rate of 600kg / h; power consumption 19kWh / t; artificial 2400kg / person class; integrated zinc powder, activator,OtherRaw materials, electricity, labor, etc.